Item | Spec | Remark |
Typical capacity | 660mAh | Discharge:1.0CmA |
Minimum capacity | 650mAh | |
Rate | 650mAh | Discharge:1200mA |
Energy | 2.41Wh | |
Nominal Voltage | 3.70V | Discharge:0.2CmA(130mA) |
AC Impedance Resistance | ≤50mΩ | |
Discharge Cut-off Voltage | 3.00V | |
Charge Voltage | 4.20V | |
Max. Charge Voltage | 4.23V | |
Charge Time | Approx 3.0h | Charge: 325mA |
Standard charge current | 130mA | 0.2CmA |
Max. Charge Current | 650mA | 1.0CmA |
Operating Temperature | 0~+45℃ | Charge |
Operating Temperature | -10~+60℃ | Discharge |
Storage Temperature | -10~+35℃ | Recommended storagetemperature: 20℃ |
Mechanical Performance | ||
Item | Measuring Procedure | Requirements |
Vibration test | After standard charge, the battery is to be tested as following conditions: Amplitude:0.19mm Frequency:10~55Hz(sweep:1Hz/min) Direction: X/Y/Z axis for 30min. The battery is to be tested in three mutually perpendicular to each axis. |
No fire, no explosion, no smoking . |
Drop Test | Drop the battery in the shipment condition(full- charge)from 1m height onto 18~20 mm or thicker concrete with p-tile on it 1 times each of obverse and inverse directions at 25±2℃ | No fire, no explosion, no smoking |
Constant Humidity and Temperature Characteristics | Under the temperature of 20±5℃, after charging the battery with 0.2C, then put the battery into the constant temperature and humidity oven with 55±2℃ and 90~95% for 48h, the battery should be no obvious deformation, leakage, rust, smoking and explosion. After testing take out the battery then rest for 2h under the temperature of 20±5℃, discharge with 1C to 3.0V. | discharge capacity≥60% C5 |
Short-Circuit Test | After standard charge, the battery is to be short-circuited by connecting the positive and negative terminals of the battery with copper wire having a maximum resistance load of 0.1Ω. | No explosion, no fire. The temperature of the exterior cell casing shall not exceed 160℃. |
Heating Test | A battery is to be heated in a gravity convection or circulating air oven. The temperature of the oven is to be raised at a rate of 5±2℃/min to a temperature of 130±2℃ at which temperature the oven is to remain for 30 minutes before the test is discontinued. | No explosion, no fire. |
Abnormal Charging Test | After standard charge, the battery is subjected to a charging current by connecting it to a dc-power supply. The beginning current is 3.0C, which is to be obtained by connecting a resistor of specified size and rating in series with the battery; the voltage of the dc-power supply is 4.6V. The test time is 2.5 hours. | No explosion, no fire. |
Overdischarge Test | The fully discharged cell is continually discharged for 24h with the (30×n) Ω load at 23±2℃. | No explosion, no fire. |